Effect of process factors on properties of high dispersion spherical alpha-Al(2)O(3 )particles prepared by hydrothermal method ( SCI-EXPANDED收录)
文献类型:期刊文献
英文题名:Effect of process factors on properties of high dispersion spherical alpha-Al(2)O(3 )particles prepared by hydrothermal method
作者:Xiang, Hairu[1];Wang, Zhiyuan[1];Yin, Qiao[1];Wang, Lei[1];Zhang, Liwei[2];Wang, Hailong[1];Xu, Hongliang[1];Zhang, Rui[1,3];Lu, Hongxia[1]
第一作者:Xiang, Hairu
通讯作者:Lu, HX[1]
机构:[1]Zhengzhou Univ, Sch Mat Sci & Engn, 100 Sci Rd, Zhengzhou 450001, Henan, Peoples R China;[2]Xinxiang Univ, Xinxiang 453003, Henan, Peoples R China;[3]Zhengzhou Univ Aeronaut, Zhengzhou 450015, Henan, Peoples R China
第一机构:Zhengzhou Univ, Sch Mat Sci & Engn, 100 Sci Rd, Zhengzhou 450001, Henan, Peoples R China
通讯机构:[1]corresponding author), Zhengzhou Univ, Sch Mat Sci & Engn, 100 Sci Rd, Zhengzhou 450001, Henan, Peoples R China.
年份:2019
卷号:45
期号:17
起止页码:22007-22014
外文期刊名:CERAMICS INTERNATIONAL
收录:;WOS:【SCI-EXPANDED(收录号:WOS:000493212500119)】;
基金:This work is supported by the National Natural Science Foundation of China numbered by 51772275 and the sponsor of the Science and Technical Development Program of Henan Province (142300410099, 172102210008).
语种:英文
外文关键词:Hydrothermal method; alpha-Al2O3 particles; Spherical morphology; Particle size regulation
摘要:Spherical alpha-Al2O3 powders were synthesized from a mixed solution consisting of Al-2(SO4)(3)center dot 18H(2)O, Al (NO3)(3)center dot 9H(2)O( )and CH4N2O by hydrothermal method with muffle calcination and microwave calcination. Effects of raw material ratio, reaction temperature, and filling factor on properties of products were investigated. Properties of thermal behavior, functional groups, phase composition, microstructure and specific surface of precursors and products were characterized by DSC-TG, FT-IR, XRD, SEM and BET, respectively. Results show that SO42- plays an important role in the sphere formation of precursors and particle size can be changed by adding different proportion of NO3-. Precursors are amorphous spherical hydrated alumina containing SO42-, and the conversion of crystalline phase is from amorphous to gamma-phase and then to alpha-phase at 1100 degrees C. Spherical morphology can be retained after crystallization to alpha-Al2O3. Compared with muffle furnace, Microwave calcination can increase calcining rate by three times and reduce insulation time by three quarters. When hydrothermal reaction temperature is 120 degrees C, the particles can be precipitated with good sphericity and narrow grain size distribution. If hydrothermal reaction temperature is too high or too low, spherical morphology can't be obtained. Size of the particles can be regulated by the different raw material ratio and filling factor from 800 nm to 3 mu m, and specific surface area is in the range of 8 m(2)/g similar to 15 m(2)/g.