柠檬酸钠对45钢锌锰系磷化膜耐蚀性能的影响
Effect of sodium citrate on corrosion resistance of zinc-manganese phosphating films on 45 steel
文献类型:期刊文献
中文题名:柠檬酸钠对45钢锌锰系磷化膜耐蚀性能的影响
英文题名:Effect of sodium citrate on corrosion resistance of zinc-manganese phosphating films on 45 steel
作者:刘贵敏[1]
第一作者:刘贵敏
机构:[1]新乡学院机电工程学院,河南新乡453000
第一机构:新乡学院机电工程学院
年份:2022
卷号:45
期号:3
起止页码:25-30
中文期刊名:兵器材料科学与工程
外文期刊名:Ordnance Material Science and Engineering
收录:CSTPCD;;北大核心:【北大核心2020】;CSCD:【CSCD_E2021_2022】;
基金:国家自然科学基金青年基金(51801171)。
语种:中文
中文关键词:柠檬酸钠浓度;锌锰系磷化膜;物相;厚度;耐蚀性能
外文关键词:concentration of sodium citrate;zinc-manganese phosphating film;phase;thickness;corrosion resistance
摘要:为降低磷化液污染,同时制备出耐蚀性能良好的锌锰系磷化膜,将环保型试剂柠檬酸钠添加到磷化液中,研究柠檬酸钠浓度对45钢表面磷化膜的形貌、物相、厚度和耐蚀性能的影响。结果表明:随柠檬酸钠浓度增加,磷化膜的物相均为Zn_(3)(PO_(4))_(2)·4H_(2)O、Mn_(2)Zn(PO_(4))_(2)·4H_(2)O和Zn_(3)Fe(PO_(4))_(2)·4H_(2)O相,但宏观和微观形貌明显变化,厚度先增后降,导致耐蚀性能先提高后下降。柠檬酸钠浓度为2 g/L时制备的锌锰系磷化膜色泽均匀且较致密,厚度最大,达8.8μm,电荷转移电阻和膜层电阻较45钢都提高了约2.6倍,表现出良好的耐蚀性能。适当增加柠檬酸钠浓度能提高磷酸盐晶体形核率,促进磷化膜结构致密,阻挡腐蚀介质侵蚀,对45钢起到较好的防腐作用,有效延缓腐蚀进程。
In order to reduce the pollution of phosphating solution and obtain a zinc-manganese phosphating film with goodcorrosion resistance,the eco-friendly reagent sodium citrate was added to the phosphating solution,and the effect ofconcentration of sodium citrate on the morphology,phase,thickness and corrosion resistance of phosphating film on 45 steel wasstudied.The results show that with the increase of concentration of sodium citrate,the phase of phosphating film is Zn_(3)(PO_(4))_(2)·4H_(2)O、Mn_(2)Zn(PO_(4))_(2)·4H_(2)O and Zn_(3)Fe(PO_(4))_(2)·4H_(2)O,but the macromorphology and micromorphology changes obviously,namely the thickness increase firstly and then decrease,and the corresponding resistance to corrosion shows a oppositetendency.The zinc-manganese phosphating film prepared with 2 g/L sodium citrate is uniform and dense,with a maximumthickness of up to 8.8μm and exhibits excellent resistance to corrosion.Its charge transfer resistance and film resistance areincreased by about 2.6 times compared with 45 steel.Appropriate increase of the concentration of sodium citrate is beneficial toincrease the nucleation rate of phosphate crystals and results in a dense structure phosphate film,enhancing the resistance to theerosion in corrosive medium and thus effectively delaying the corrosion process and exerting a superior protective effect on 45steel.